Structural and Mechanical Properties of Hydrodynamically Activated Wood Pulp in Additive Technologies
DOI:
https://doi.org/10.37482/0536-1036-2023-2-121-131Keywords:
humidity of wood pulp, homogeneity of wood pulp, plastometer, creep limit, additive technologies, mixture extrusion, self-adhesion, piezothermic influence, 3D printingAbstract
One of the techniques of additive technologies is 3D printing. It is a perspective direction in the development of low-rise housing construction. The process of 3D printing can be performed with various materials. Although this study investigates the possibility of applying hydrodynamically activated wood pulp. A fragmentated wood in the process of activation changes physical and chemical properties because of the cavitation effect. Such fragments in the form of the activated pulp are a solid dispersed system, whose properties depend on humidity. The activated pulp mass is created by moisture elimination, and it can be transported through pipelines. The structure is formed in the process of self-adhesion, without any adhesives, by the appearance of autogenous interactions between the wood particles. The obtained material has a sufficiently high strength and water resistance, which are the prerequisites for the use of activated wood pulp in additive technologies. The 3D printed products are constructed by applying some material in layers at certain time intervals. The main requirements are a steady shape and a homogeneity of the structure. Therefore, the limit of creep rate for the pulp mass was determined that is a yield tensile stress point, above which the material (flow) undergoes an intensive plastic deformation. In this study, a conical plastometer was used according to the method of Academician P.A. Rebinder. The measured parameter depends significantly on the humidity of the pulp. There found an inverse relationship between the humidity and the creep limit. The obtained dependence is fundamental for determination of the thickness of applied layers and the time intervals between applications. The homogeneity of the structure in the interlayer section determines the strength of the entire product. It is obtained when the humidity level is greater than 400 % in the contact area. The high humidity level at the contact area with the low average humidity of the material can be created by microwave radiation treatment. Thus, the moisture is distributed across the thickness of the layer. The treatment also increases the humidity level on the surface and reduces it in the center of the material.
For citation: Ermolin V.N., Bayandin M.A., Namyatov A.V., Ostryakova V.A. Structural and Mechanical Properties of Hydrodynamically Activated Wood Pulp in Additive Technologies. Lesnoy Zhurnal = Russian Forestry Journal, 2023, no. 2, pp. 121–131. (In Russ.). https://doi.org/10.37482/0536-1036-2023-2-121-131
Downloads
References
Аведиков А.С., Остриков М.С., Дибров Г.Д. Об усадочном напряжении в дисперсных структурах // Докл. АН СССР. 1965. Т. 163, № 5. С. 1185–1188. Avedikov A.S., Ostrikov M.S., Dibrov G.D. Contraction Stress in Dispersed Structures. Doklady Akademii nauk USSR. Chemistry Series, 1965, vol. 163, no. 5, pp. 1185–1188. (In Russ.).
Артёмов А.В., Бурындин В.Г., Савиновских А.В. Влияние карбамида на физико-механические свойства пластика на основе сосновых опилок // Вестн. технол. ун-та. 2021. Т. 24, № 5. С. 35–39. Artemov A.V., Buryndin V.G., Savinovskikh A.V. The Influence of Carbamide on the Physico-Mechanical Properties of Plastic Made of Pine Sawdust. Vestnik of Kazan National Research Technological University, 2021, vol. 24, no. 5, pp. 35–39. (In Russ.).
Базарнова Н.Г., Маркин В.И., Катраков И.Б., Колосов П.В., Калюта Е.В., Чепрасова М.Ю. Методы получения лигноуглеводных композиций из химически модифицированного растительного сырья // Рос. хим. журн. 2011. Т. 55, № 1. С. 4–9. Bazarnova N.G., Markin V.I., Katrakov I.B., Kolosov P.V., Kalyuta E.V., Cheprasova M.Yu. Methods for Obtaining Lignocarbohydrate Compositions from Chemically Modified Plant Raw Materials. Rossiyskiy khimicheskiy zhurnal, 2011, vol. 55, no. 1, pp. 4–9. (In Russ.).
Ефремов А.А. Влияние условий термокаталитической активации древесины осины на состав водорастворимых продуктов // Химия природ. соединений. 1995. № 6. С. 20–25. Efremov A.A. Influence of the Conditions for Thermocatalytic Activation of Aspen Wood on the Composition of Water-Soluble Products. Khimiya prirodnykh soyedineniy = Chemistry of Natural Compounds, 1995, no. 6, pp. 20–25. (In Russ.).
Казицин С.Н. Получение древесных плит без связующих веществ из механо-активированных древесных частиц: дис. … канд. техн. наук. Екатеринбург, 2017. 132 с. Kazitsin S.N. Production of Chipboards Without Binders from Mechanically Activated Wood Particles: Cand. Eng. Sci. Diss. Ekaterinburg, 2017. 132 р. (In Russ.).
Карасев Е.И., Киселев И.Ю., Мерсов Е.Д., Киселева Г.В. Водостойкость древесноволокнистых плит. М.: ВНИПИЭИлеспром, 1986. 32 с. Karasev E.I., Kiselev I.Yu., Mersov E.D., Kiseleva G.V. Water Resistance of Wood Fibreboards. Moscow, VNIPIEIlesprom Publ., 1986. 32 p. (In Russ.).
Кондрашенко В.И., Тарарушкин Е.В., Горшина Е.С., Кесарийский А.Г. Биопластики – древесные композиционные материалы, получаемые методами биотехнологии // Вестн. ДонНАСА. 2012. № 1(93). С. 17–24. Kondrashenko V.I., Tararushkin E.V., Gorshina E.S., Kesariyskiy A.G. Bioplasics – Wood Composites Obtained by Biotechnology Methods. Vestnik of DonNACA, 2012, no. 1(93), pp. 17–24. (In Russ.).
Намятов А.В., Баяндин М.А., Казицин С.Н., Ермолин В.Н. Исследование свойств плит малой плотности из механоактивированных древесных частиц без использования связующих веществ // Строение, свойства и качество древесины – 2018: материалы VI Междунар. симп. им. Б.Н. Уголева, посвящ. 50-летию Регионального Координационного совета по современным проблемам древесиноведения, Красноярск, 10–16 сент. 2018 г. Новосибирск: СО РАН, 2018. С. 149–151. Namyatov A.V., Bayandin M.A., Kazitsin S.N., Ermolin V.N. Investigation of the Properties of Low-Density Boards Made of Mechanically Activated Wood Particles Without Usage of Binders. Structure, Properties and Quality of Wood – 2018: Proceedings of the 6th International Symposium named after B.N. Ugolev, dedicated to the 50th anniversary of the Regional Coordinating Council on Modern Problems of Wood Science. Krasnoyarsk, September 10-16, 2018. Novosibirsk, SB RAS, pp. 149–151. (In Russ.).
Ребиндер П.А. Поверхностные явления в дисперсных системах. Физико-химическая механика. Избр. тр. М.: Наука, 1979. 384 с. Rebinder P.A. Surface Effects in Dispersed Systems. Physico-Chemical Mechanics. Selected Works. Moscow, Nauka Publ., 1979. 384 p. (In Russ.).
Bos F., Wolfs R., Ahmed Z., Salet T. Additive Manufacturing of Concrete in Construction: Potentials and Challenges of 3D Concrete Printing. Virtual and Physical Prototyping, 2016, vol. 11, no. 3, pp. 209–225. https://doi.org/10.1080/17452759.2016.1209867
Correa D., Papadopoulou A., Guberan C., Jhaveri N., Reichert S., Menges A., Tibbits S. 3D printed Wood: Programming Hygroscopic Material Transformations. 3D Printing and Additive Manufacturing, 2015, vol. 2, no. 3, pp. 106–116. https://doi.org/10.1089/3dp.2015.0022
Feng P., Meng X., Chen J.-F., Ye L. Mechanical Properties of Structures 3D Printed with Cementitious Powders. 3D Concrete Printing Technology, Elsevier, 2019, pp. 181–209. https://doi.org/10.1016/B978-0-12-815481-6.00009-9
Ferretti E., Moretti M., Chiusoli A., Naldoni L., de Fabritiis F., Visonà M. Rice-Husk Shredding as a Means of Increasing the Long-Term Mechanical Properties of Earthen Mixtures for 3D Printing. Materials, 2022, vol. 15, no. 3, p. 743. https://doi.org/10.3390/ma15030743
Forss K. Biotechnology in the Forest Industry. Bioconversion of Plant Raw Material by Microorganisms: Proceedings of the 5th Finnish-Soviet Seminar. Helsinki, University of Helsinki, 1983, pp. 13–21.
Kirk T.K., Shimada M. Lignin Biodegradation: The Microorganisms Involved and the Physiology and Biochemistry of Degradation by White-Rot Fungi. Biosynthesis and Biodegradation of Wood Components, Elsevier, 1985, pp. 579–605. https://doi.org/10.1016/B978-0-12-347880-1.50025-8
Le Duigou A., Castro M., Bevan R., Martin N. 3D Printing of Wood Fibre Biocomposites: From Mechanical to Actuation Functionality. Materials and Design, 2016, vol. 96, pp. 106–114. https://doi.org/10.1016/j.matdes.2016.02.018
Min K.-S., Park K.-M., Lee B.-C., Roh Y.-S. Chloride Diffusion by Build Orientation of Cementitious Material-Based Binder Jetting 3D Printing Mortar. Materials, 2021, vol. 14, no. 23, p. 7452. https://doi.org/10.3390/ma14237452
Perrot A., Rangeard D., Pierre A. Structural Built-Up of Cement-Based Materials Used for 3D Printing Extrusion Techniques. Materials and Structures, 2016, vol. 49, no. 4, pp. 1213–1220. https://doi.org/10.1617/s11527-015-0571-0
Unbehaun H., Konig S., Spindler D., Kerns G. Enzymatic Modification of Lignocellulosic Substances for the Production of Fiberboards. Moscow University Chemistry Bulletin, 2008, vol. 63, no. 2, pp. 126–130. https://doi.org/10.3103/S002713140802017X
Velásquez J.A., Ferrando F., Salvadó J. Binderless Fiberboard from Steam Exploded Miscanthus Sinensis: The Effect of a Grinding Process. European Journal of Wood and Wood Products, 2002, vol. 60, no. 4, pp. 297–302. https://doi.org/10.1007/s00107-002-0304-2
Velásquez J.A., Ferrando F., Salvadó J. Binderless Fiberboard from Steam Exploded Miscanthus Sinensis: Optimization of Pressing and Pretreatment Conditions. Wood Science and Technology, 2003, vol. 37, no. 3-4, pp. 279–286. https://doi.org/10.1007/s00226-003-0186-4